Chemi-mechanical pulping was evaluated as a potential way to prepare sugarcane bagasse fibers for papermaking. Cellulose, lignin, ash, and extractives soluble in alcohol-acetone were measured as 55.75%, 20.5%, 1.85%, and 3.25%, respectively. Fiber length, diameter, lumen cavity, and cell wall thickness were measured as 1.59 mm, 20.96, 9.72, and 5.64 μm. The chemi-mechanical pulping conditions were selected as follows: three charging levels of 10, 15, and 20% sodium sulphite, and three pulping times of 20, 30, and 40 minutes after reaching the pulping temperature. Pulping temperature was held constant at 165 C. Different pulping conditions resulted in pulp yields between 65.38 and 84.28%. The highest yield (84.28%) was obtained using a treatment combination of 20 minutes pulping time and 10% sodium sulphite. The lowest yield (65.38%) was related to 40 minutes pulping time and 20% sodium sulphite. Pulps were refined to 300 ± 25 mL CSF, 60 gm-2 handsheets were made, and then strength indices and optical properties of the handsheets were measured. The results showed that 20% sodium sulphite, 40 minutes pulping time, at 165 ºC can be considered as the optimum pulping conditions for bagasse CMP pulping. Tensile, tear, and burst strength indices, as well as the opacity of this pulp were measured as 39.59 Nmg-1, 6.66 mNm2g-1, 2.1 KPa m2g-1, and 95.35%, respectively.
کلید واژگان :Bagasse; CMP; Yield; Tear index; Tensile index; Opacity; Fiber length
ارزش ریالی : 600000 ریال
با پرداخت الکترونیک