It was found out that the logarithmic models fit the cement–slag blend systems well. In the present study, based on the experimental results, a logarithmic model has been developed to predict the compressive strength of chemically activated high phosphorous slag content cement. Mixes of phosphorous slag (80 wt.%), Portland cement (14 wt.%) and compound chemical activator (6 wt.%) were prepared at different Blaine finenesses using a laboratory ball mill. Compressive strengths of mortar specimens cured in lime-saturated water were measured at different curing times. Mathematical model was prepared in terms of curing time and water-to-cement ratio as independent variables and compressive strength as dependent variable. The comparisons between the model reproductions and the experimentally obtained results confirm the applicability of the presented model.
کلید واژگان :Phosphorous slag, Compressive strength, Water-to-cement ratio, Modeling