Size Controlling of L10-FePt Nanoparticles During High Temperature Annealing on the Surface of Carbon Nanotubes

Mono-size FePt nanoparticles with particles size about 2.5 nm have been prepared by polyol method on the surface of carbon nanotubes (CNTs). The CNTs functinalization time and the mass ratio of nanoparticles to CNTs affects on the CNTs surface coating. The as-synthesis nanocomposites have a superparamagnetic behavior with chemically disordered fcc structure at room temperature and they can be transformed into chemically ordered fct structure after thermal annealing above 600 C. Their magnetic behavior changes from the superparamagnetic to the ferromagnetic with a large coercivity up to 0.83 T for the nanocomposites which annealed at 800 C. The CNTs surfaces as a substrate prevent the agglomeration of nanoparticles during high temperature annealing and the FePt nanoparticles after annealing at 800 C have finite size with an average about 10 nm. The structure, composition and magnetic properties of nanocomposite were characterized by X-ray diffraction, transmission electron microscopy, Fourier transform infrared spectroscopy and vibrating sample magnetometer.

FePt nanoparticles ; Carbon nanotubes; Nanocomposites ; Ordering parameter ; Superparamagnetic ; Ferromagnetic ; fcc and fct L10 structure