A huge amount of carbon dioxide is released in the Portland cement production process. A large quantity of greenhouse gases is produced because of the significant amount of energy consumption via making bricks through firing. Using the pozzolanic sources containing the aluminosilicate and alkaline reagents, a new type of green materials called geopolymeric materials are produced with quite lower environmental hazards. The use of laterite as an iron-rich aluminosilicate material has a high potential for building materials. In this study, the effect of the curing temperature and characteristics of the alkaline reagent including the concentration of sodium hydroxide solution and the water-glass to sodium hydroxide mass mixing ratio on the mechanical strength of the laterite-based, oven-cured geopolymer samples was investigated. The results showed that the curing temperature had a significant effect on the compressive strength of the laterite-basedJournal of Engg. Research Online First Article 2 geopolymer samples so that with a 15°C change at the curing temperature, the compressive strength of the samples could be multiplied and a sharp increase in the mechanical strength could occur. Also, according to the results of this study, the 6 M sodium hydroxide is recommended for the construction of the laterite-based geopolymer materials with low cost and relatively high strength, and for the construction of higherstrength building materials, the 14 M sodium hydroxide is recommended.
کلید واژگان :Geopolymer; Laterite; Alkali activated; Curing Temperature; Mechanical strength
ارزش ریالی : 600000 ریال
با پرداخت الکترونیک